|15ГС, 16ГС |ОСТ 108.030.113-87|ОСТ 108.030.113-87| -"- | 450 | +| + | + | + | + | + | + | + |
|-----------+------------------+------------------+-----------+------+--+---+---+---+----+---+--------+---------|
|16ГНМА |ОСТ 108.030.113-87|ОСТ 108.030.113-87| -"- | 350 | +| + | + | + | + | + | + | + |
|-----------+------------------+------------------+-----------+------+--+---+---+---+----+---+--------+---------|
| 12МХ |ГОСТ 8479-70 |ГОСТ 20072-74 | -"- | 530 | +| + | + | + | + | + | - | + |
| |(група ІV, V) | | | | | | | | | | | |
|-----------+------------------+------------------+-----------+------+--+---+---+---+----+---+--------+---------|
| 15 ХМ |ГОСТ 8479-70 |ГОСТ 4543-71 | -"- | 550 | +| + | + | + | + | + | - | + |
| |(група ІV, V) | | | | | | | | | | | |
|-----------+------------------+------------------+-----------+------+--+---+---+---+----+---+--------+---------|
|12Х1МФ |ОСТ 108.030.113-87|ОСТ 108.030.113-87| -"- | 570 | +| + | + | + | + | + | + | + |
|-----------+------------------+------------------+-----------+------+--+---+---+---+----+---+--------+---------|
|15Х1М1Ф |ОСТ 108.030.113-87|ОСТ 108.030.113-87| -"- | 575 | +| + | + | + | + | + | + | + |
-----------------------------------------------------------------------------------------------------------------
Примечания:
1. Круглый прокат, используемый в соответствии с пунктом 9.25 настоящих Правил, допускается использовать согласно НД на прокат на условиях, указанных в разделе 4, т.е. делать из тех же марок стали, на те же параметры, при выполнении того же контроля механических свойств (на растяжение и ударную вязкость) и сплошного радиографического контроля или УЗК. Если диаметр проката более 80 мм, то контроль механических свойств необходимо проводить на образцах тангенциального направления.
2. Нормируемые показатели и объем контроля сварных труб должны соответствовать требованиям, указанным в НД. Категория, группа качества поковок и дополнительные испытания, предусмотренные НТД, выбираются конструкторской организацией. Требования, предусмотренные в разделе 4 (знак +), но отсутствующие в действующих НД, выполнены изготовителем элементов трубопровода.
(3). Контроль механических свойств при испытаниях на растяжение производится в соответствии с пунктами 9.9 и 9.14, а при испытаниях на ударную вязкость - в соответствии с пунктами 9.10 - 9.12.
4. Все поковки деталей трубопроводов I и II категорий, имеющие один из габаритных размеров более 200 мм и толщину более 50 мм, подлежат радиографическому контроля или УЗК.
5. Разрешается использование поковок из сталей 20, 25 и 12Х1МФ по ГОСТ 8479-70 (группа II) при Dу <100 мм без ограничения давления, при температурах до 350 град.С для сталей 20 и 25 и до 570 град.С для стали 12Х1МФ.
(6). Материал для поковок и штамповок из листовой стали должен соответствовать требованиям, указанным в листовой стали в разделе I приложения 2 Правил.
V. Стальные отливки
--------------------------------------------------------------------------------------------------------
| | НД |Граничні параметри| Обов'язкові механічні|Дефек-|
| | | | випробування(1, 2) |тоско-|
| Марка |-------------------------------------+------------------+-----------------------|пія(3)|
| сталі |на виловок |на сталь |р, МПа |t, |&в|&т | б | V | КС | Н | |
| | | |(кгс/кв.см)|град.С| | | | | | | |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 1 | 2 | 3 | 4 | 5 | 6| 7 | 8 | 9 | 10 | 11| 12 |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
|15Л, 20Л, 25Л,|ГОСТ 977-88 |ГОСТ 977-88 | 5 (50) | 300 | +| + | + | - | - | - | - |
|30Л, 35Л |(група 2) | | | | | | | | | | |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
|20Л, 25Л, |ГОСТ 977-88 |ГОСТ 977-88 |не обмежено| 350 | +| + | + | - | + | - | + |
|30Л, 35Л |(група 3) | | | | | | | | | | |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 25Л |ОСТ 108.961.03-79 |ОСТ 108.961.03-79 | -"- |425(4)| +| + | + | + | + | + | + |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 20ГСЛ |ОСТ 108.961.03-79 |ОСТ 108.961.03-79 | -"- | 450 | +| + | + | + | + | + | + |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 20ХМЛ |ОСТ 108.961.03-79 |ОСТ 108.961.03-79 | -"- | 520 | +| + | + | + | + | + | + |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 20ХМФЛ |ОСТ 108.961.03-79 |ОСТ 108.961.03-79 | -"- | 540 | +| + | + | + | + | + | + |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
| 15Х1М1ФЛ |ОСТ 108.961.03-79 |ОСТ 108.961.03-79 | -"- | 570 | +| + | + | + | + | + | + |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
|12Х18Н9ТЛ |ГОСТ 977-88 |ГОСТ 977-88 | -"- | 610 | +| + | + | + | + | - | + |
| |(група 3) |(група 3) | | | | | | | | | |
|--------------+------------------+------------------+-----------+------+--+---+---+---+----+---+------|
|12Х18Н12М3ТЛ |ГОСТ 977-88 |ГОСТ 977-88 | -"- | 610 | +| + | + | + | + | - | + |
| |(група 3) |(група 3) | | | | | | | | | |
--------------------------------------------------------------------------------------------------------
Примечания:
1. Нормируемые показатели и объем контроля должны соответствовать указанным в НД. Группа качества и дополнительные виды испытаний, предусмотренные НТД, выбираются конструкторской организацией. Требования, предусмотренные в разделе 5 (знак +), но отсутствующие в действующих НД, выполнены изготовителем элементов трубопровода.
2. Контроль механических свойств при испытаниях на растяжение производится в соответствии с пунктами 9.9 и 9.14, а при испытаниях на ударную вязкость - в пункты 9.10 - 9.12.
(3). Отливки для трубопроводов I и II категорий подлежат радиографическому контроля, УЗК или другому равноценном контроля. Объем контроля устанавливается техническими условиями на отливки. При этом обязательному контролю подлежат конце патрубков, которые свариваются.
4. Для отливок, изготавливаемых в соответствии с требованиями ОСТ 108.961.03-79 из стали 25Л с толщиной стенки в позафланцевий части до 55 мм, предельная температура их использования устанавливается до 450 град.С.
VI. Крепление
-----------------------------------------------------------------------------------------------------------------------
| | НД |Граничні параметри робочого середовища| Обов'язкові |Мак- |
| | | | випробування(1) |рост-|
| Марка |---------------------------------+--------------------------------------+-----------------------|рук- |
| сталі |на кріплення |на сталь | шпильки(2) і | гайки(4) |механічні (шпильок і |тура |
| | | | болти(3) | |болтів(5)) | |
| | | |------------------+-------------------+-----------------------| |
| | | |р, МПа |t, |р, МПа |t, |&в|&т | б | V | КС | Н | |
| | | |(кгс/кв.см)|град.С|(кгс/кв.см)|град.С | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8| 9 | 10| 11| 12 | 13| 14 |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|Ст5сп2 | | | | | | | | | | | | | |
|Ст3сп3 |ГОСТ 20700-75 |ГОСТ 380-886(6)| 2,5 (25) | 200 | 2,5 (25) | 350 | +| + | + | - | - | - | - |
|Ст4сп3 | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|Ст3сп6 |ГОСТ 20700-75 |ГОСТ 380-88(6) | 1,6 (16) | 350 | -"- | -"- | +| + | + | - | + | - | - |
|Ст3сп5 | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|Ст3сп3 | | | | | | | | | | | | | |
|Ст3пс3(7) |ГОСТ 1759.0-87(7)|ГОСТ 380-88(6) | --- | --- | -"- | -"- | -| - | - | - | - | + | - |
|Ст3кп3(7) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|10, 10кп |ГОСТ 20700-75 |ГОСТ 1050-88 | --- | --- | -"- | -"- | -| - | - | - | - | + | - |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| 20 |ГОСТ 20700-75 |ГОСТ 1050-88 | 2,5 (25) | 400 | 10,0 (100)| 400 | +| + | + | + | + | + | - |
| |ГОСТ 1759.0-87(7)|ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| 25 |ГОСТ 20700-75 |ГОСТ 1050-88 | 2,5 (25) | -"- | -"- | -"- | +| + | + | + | + | + | - |
| | |ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|30, 35, 40 |ГОСТ 20700-75 |ГОСТ 1050-88 | 10,0 (100)| 425 | 20,0 (200)| 425 | +| + | + | + | + | + | - |
| |ГОСТ 1759.0-87(7)|ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| 45 |ГОСТ 20700-75 |ГОСТ 1050-88 | 10,0 (100)| -"- | -"- | -"- | +| + | + | + | + | + | - |
| | |ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|09Г2С |ОСТ 26-.2043-91 |ГОСТ 19281-89 | 10,0 (100)| -"- | --- | --- | +| + | + | + | + | + | + |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|35Х, 40Х |ГОСТ 20700-75 |ГОСТ 4543-71 | 20,0 (200)| -"- | 20,0 (200)| 450 | +| + | + | + | + | + | + |
| | |ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|30ХМА, 35ХМ |ГОСТ 20700-75 |ГОСТ 4543-71 |Не обмежено| 450 |Не обмежено| 510 | +| + | + | + | + | + | + |
| | |ГОСТ 10702-78 | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|38ХН3МФА | ГОСТ 23304-78 |ГОСТ 4543-71 |Не обмеж. | 350 | Не обмеж.| 350 | +| + | + | + | + | + | + |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|25Х1МФ | ГОСТ 20700-75 |ГОСТ 20072-75 | -"- | 510 | -"- | 540 | +| + | + | + | + | + | + |
| (ЭИ10) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|20Х1М1Ф1ТР | ГОСТ 20700-75 |ГОСТ 20072-75 | -"- | 580 | -"- | 580 | +| + | + | + | + | + | + |
| (ЭП182) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|20Х1М1Ф1БР | ГОСТ 20700-75 |ГОСТ 20072-75 | -"- | -"- | -"- | -"- | +| + | + | + | + | + | + |
|(ЕП44) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| 20Х13 | ГОСТ 20700-75 |ГОСТ 18968-72 | -"- | 450 | -"- | 510 | +| + | + | + | + | + | + |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|13Х11Н2В2МФ | ГОСТ 20700-75 |ГОСТ 5949-75 | -"- | 510 | -"- | 540 | +| + | + | + | + | + | + |
|(ЭИ961) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|20Х12ВНМФ | ГОСТ 20700-75 |ГОСТ 28969 | -"- | 560 | -"- | 560 | +| + | + | + | + | + | + |
|(ЭП428) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|18Х12ВМБФР | ГОСТ 20700-75 |ГОСТ 5949-75 | -"- | -"- | -"- | -"- | +| + | + | + | + | + | + |
|(ЭИ993) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|08Х16Н13М2Б | ГОСТ 20700-75 |ГОСТ 5632-72 | -"- | 625 | -"- | 625 | +| + | + | + | + | + | + |
|(ЭП680) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
|31Х19Н9МВБТ | ГОСТ 20700-75 |ГОСТ 5632-72 | -"- | -"- | -"- | -"- | +| + | + | + | + | + | + |
|(ЭИ572) | | | | | | | | | | | | | |
|--------------+-----------------+---------------+-----------+------+-----------+-------+--+---+---+---+----+---+-----|
| ХН35ВТ | ГОСТ 20700-75 |ГОСТ 5632-72 | -"- | 650 | -"- | 650 | +| + | + | + | + | + | + |
| (ЭИ612) | | | | | | | | | | | | | |
-----------------------------------------------------------------------------------------------------------------------
Примечания:
1. Нормируемые показатели и объем контроля должны соответствовать указанным в стандартах. Категории, группы качества и дополнительные испытания, предусмотренные стандартами, выбираются конструкторской организацией. Требования, предусмотренные в разделе 6 (знак +), но отсутствующие в действующих НД, выполнены изготовителем элементов трубопровода.
2. Использование шипов по ГОСТ 1759.0-87 допускается до температуры 300 град.С.
(3). Использование болтов разрешается по ГОСТ 20700-75 давлением до 3 МПа (30 кгс / кв.см) и температуре 400 град.С и ГОСТ 1759.0-87 давлением до 3 МПа (30 кгс / кв.см и температуре 300 град.С. В других случаях должны использоваться шпильки.
4. Материал для гаек контролируемого только на твердость.
5. Контроль механических свойств при испытаниях на растяжение производится в соответствии с пунктами 9.9 и 9.14, а при испытаниях на ударную вязкость - в пункты 9.10 - 9.13.
(6). Материал шпилек, болтов из углеродистых сталей зигдно ГОСТ 380-88, предназначенные для работы при температуре выше 200 град.С, необходимо испытывать на ударную вязкость после механического старения.
(7). Гайки из полуспокойной и кипящей стали допускается использовать, если температура в помещении, где установлено оборудование, больше 0 град.С. Согласно ГОСТ 1759.4-87 и ГОСТ 1759.5-87 следует использовать болты и шпильки из стали 20 классов прочности 4 или 5, из сталей 30 и 35 - классов прочности 5 или 6; гайки из сталей Ст3 и 20 - класса прочности 4, сталей 30 и 35 - класса прочности 5.
(8). Для шпилек, болтов из аустенитных сталей накатывания резьбы является допустимым при температуре среды до 500 град.С.
VII. Чугунные
---------------------------------------------------------------------------------
|Марка чавуну | НД | Граничні параметри |Обов'язкові механічні|
| | | | випробування(1) |
| | |----------------------------+---------------------|
| | |Dу, мм|t, град.С|р, МПа | &в | &т | б | Н |
| | | | |(кгс/кв.см)| | | | |
|---------------+------------+------+---------+-----------+----+----+-----+-----|
|Сч10(2), Сч15 |ГОСТ 1412-83| 80 | 130 | 3,0 (30) | + | - | - | + |
| | | 300 | 200 | 0,8 (80) | | | | |
|---------------+------------+------+---------+-----------+----+----+-----+-----|
|Сч20, Сч25, |ГОСТ 1412-83| 100 | 300 | 3,0 (30) | | | | |
|Сч30, Сч35 | | 200 | | 1,3 (13) | + | - | - | + |
| | | 300 | | 0,8 (80) | | | | |
| | | 600 | 130 | 0,64 (6,4)| | | | |
| | |1000 | | 0,25 (2,5)| | | | |
|---------------+------------+------+---------+-----------+----+----+-----+-----|
|Кч33-08, Кч35- |ГОСТ 1215-79| 200 | 300 | 1,6 (16) | + | - | + | + |
|10, Кч37-12 | | | | | | | | |
|---------------+------------+------+---------+-----------+----+----+-----+-----|
|Вч35, Вч40,Вч45|ГОСТ 7293-85| 200 | 350 | 4,0 (40) | + | + | + | + |
| | | 600 | 130 | 0,8 (80) | | | | |
---------------------------------------------------------------------------------
Примечания:
1. Нормируемые показатели и объем контроля должны соответствовать указанным в стандартах.
2. Использование чугуна СЧ10 разрешается с временным сопротивлением не ниже 120 МПа (12 кгс / кв.мм).
Приложение 3
с пунктом 9.1. Правил устройства и
безопасной эксплуатации трубопроводов
пара и горячей воды
Подразделение сталей на типы и классы
----------------------------------------------------------------------------
|NN | Тип, клас сталі | Марка сталі |
|з/п| | |
|---+------------------------------------+---------------------------------|
| 1 |Вуглецеві |Ст2сп2, Ст2сп3, Ст3сп2, Ст3сп3, |
| | |Ст3пс3, Ст3Гпс3, Ст3пс4, Ст3сп4, |
| | |Ст3сп5, Ст2сп6, Ст3Гпс4, Ст4пс3, |
| | |Ст4сп3, Ст5сп2*, 08, 10, 15, 20, |
| | |25, 30*, 35*, 40*, 15К, 16К, 18К,|
| | |20К, 22К, 15Л, 20Л, 30Л, 35Л |
|---+------------------------------------+---------------------------------|
| 2 |Низьколеговані марганцевисті і крем-|10Г2, 15ГС, 16ГС, 17ГС, 17Г1С, |
| |ніймарганцевисті |17Г1СУ, 09Г2С, 10Г2С1, 14ХГС |
|---+------------------------------------+---------------------------------|
| 3 |Низьколеговані хромисті |35Х*, 40Х* |
|---+------------------------------------+---------------------------------|
| 4 |Низьколеговані молібденові, хромомо-|12МХ, 12ХМ, 15ХМ, 10Х2М, 15Х1М1Ф,|
| |лібденові та хромомолібденованадієві|12Х1МФ, 20ХМЛ, 20 ХМФЛ, 15Х1МФЛ, |
| | |20Х1МФ*, 25Х1М1Ф1ТР*, 20Х1М2Ф1БР*|
|---+------------------------------------+---------------------------------|
| 5 |Низьколеговані хромонікельмолібдено-|38ХН3МФА* |
| |ванадієві | |
|---+------------------------------------+---------------------------------|
| 6 |Мартенситні хромисті |20Х13, 12Х11В2МФ*, 13Х11М2В2МФ*, |
| | |20Х12ВНМФ*, 18Х12ВМВФР* |
|---+------------------------------------+---------------------------------|
| 7 |Аустенітні хромонікелеві |08Х18Н10Т, 12Х18Н9Т, 12Х18Н10Т, |
| | |12Х18Н12Т, 12Х18Н9ТЛ, |
| | |12Х18Н12М3ТЛ, ХН35ВТ |
----------------------------------------------------------------------------