ДСТУ EN 10213:2015 сторінка 2 з 5
e) hardness test (not applicable);
-
f) homogeneity of test units (hardness test);
-
g) pressure or leak testing;
-
h) intergranular corrosion test (according to EN ISO 3651-2);
-
i) tests for magnetic properties;
-
j) other tests for any other properties shall be agreed.
-
8.6 Invalidation of tests
-
8.7 Retests
-
8.8 Sorting and reprocessing9 Marking
-
10 Packaging and surface protection
-
11 Complaints
12 Supplementary information
Information on physical properties and creep properties of the steel grades are given in Annex В and Annex C.Table 2 — Chemical composition (cast analysis) (% by mass)
|
Ferritic and martensitic |
Designation |
C |
Si |
Mn |
P Max. |
s max. |
Cr |
Mo |
Ni |
Cu |
N |
V |
Others |
|||||||||||||
|
Name |
Number |
|||||||||||||||||||||||||
|
GP240GH |
1.0619 |
0,18 to 0,23 |
0,60 max |
0,50 to 1,20 |
0,030 |
0,020 a |
0,30 b max |
0,12 b max |
0,40 b max. |
0,30 max. b |
0,03 b max |
|||||||||||||||
|
GP280GH |
1.0625 |
0,18 to 0,25 c |
0,60 max |
0.80 to 1.20 c |
0,030 |
0,020 a |
0,30 b max |
0,12 b max. |
0,40 b max |
0,30 b max. |
0,03 b max |
|||||||||||||||
|
G17Mn5 |
1.1131 |
0,15to0,20 |
0,60 max |
1,00 to 1,60 |
0,020 |
0,020 a |
0,30 b max. |
0,12 b max. |
0,40 b max. |
0,30 max. b |
0,03 b max. |
|||||||||||||||
|
G20Mn5 |
1.6220 |
0,17 to 0,23 |
0,60 max |
1,00 to 1,60 |
0,020 |
0,020 3 |
0,30 max. |
0,12 max. |
0,80 max. |
0,30 max. |
0,03 max. |
|||||||||||||||
|
G18Mo5 |
1.5422 |
0,15 to 0,20 |
0,60 max |
0,80 to 1,20 |
0,020 |
0,020 |
0,30 max. |
0,45 to 0,65 |
0,40 max. |
0,30 max |
- |
0,05 max |
||||||||||||||
|
G20Mo5 |
1.5419 |
0,15 to 0,23 |
0,60 max |
0,50 to 1,00 |
0,025 |
0,020 а |
0,30 max. |
0,40 to 0,60 |
0,40 max. |
0,30 max. |
0,05 max. |
* |
||||||||||||||
|
G17CrMo5-5 |
1.7357 |
0,15 to 0,20 |
0,60 max |
0,50 to 1,00 |
0,020 |
0,020 a |
1,00 to 1,50 |
0,45 to 0,65 |
0,40 max. |
0,30 max. |
0,05 max. |
|||||||||||||||
|
G17CrMo9-10 |
1.7379 |
0,13 to 0,20 |
0,60 max |
0,50 to 0,90 |
0,020 |
0,020 a |
2,00 to 2,50 |
0,90 to 1,20 |
0,40 max |
0,30 max. |
0,05 max. |
|||||||||||||||
|
G12MoCrV5-2 |
1.7720 |
0,10to0,15 |
0,45 max |
0,40 to 0,70 |
0,030 |
0,020 a |
0,30 to 0,50 |
0,40 to 0,60 |
0,40 max. |
0,30 max |
0,22 to 0,30 |
Sn: 0,025 max. |
||||||||||||||
|
G17CrMoV5-10 |
1.7706 |
0,15to0,20 |
0,60 max |
0,50 to 0,90 |
0,020 |
0,015 |
1,20 to 1,50 |
0,90 to 1,10 |
0,40 max |
0,30 max. |
- |
0,20 to 0,30 |
Sn: 0,025 max. |
|||||||||||||
|
G9Ni10 |
1.5636 |
0,06 to 0,12 |
0,60 max. |
0,50 to 0,80 |
0,020 |
0,015 |
0,30 max. |
0,20 max. |
2,00 to 3,00 |
0,30 max. |
0,05 max. |
|||||||||||||||
|
G17NiCrMo13-6 |
1.6781 |
0,15 to 0,19 |
0,50 max. |
0,55 to 0,80 |
0.015 |
0,015 |
1,30 to 1,80 |
0,45 to 0,60 |
3,00 to 3,50 |
0,30 max. |
0,05 max. |
|||||||||||||||
|
G9Ni14 |
1.5638 |
0,06 to 0,12 |
0,60 max |
0,50 to 0,80 |
0,020 |
0,015 |
0,30 max. |
0,20 max. |
3,00 to 4,00 |
0,30 max |
0,05 max |
|||||||||||||||
|
GX15CrMo5 |
1 7365 |
0,12to0,19 |
0.80 max |
0,50 to 0,80 |
0,025 |
0,025 |
4,00 to 6,00 |
0,45 to 0,65 |
0,30 max |
0,05 max |
||||||||||||||||
|
GX8CrNi12 |
1.4107 |
0,10 max. |
0,40 max. |
0,50 to 0,80 |
0,030 |
0,020 |
11,50 to 12,50 |
0,50 max. |
0,80 to 1,50 |
0,30 max. |
- |
0,08 max. |
||||||||||||||
|
GX3CrNi13-4 |
1 6982 |
0,05 max. |
1,00 max |
1,00 max. |
0,035 |
0,015 |
12,00 to 13,50 |
0,70 max. |
3,50 to 5,00 |
0,30 max |
0,08 max. |
|||||||||||||||
|
GX4CrNi13-4 |
1.4317 |
0,06 max. |
1,00 max |
1,00 max. |
0,035 |
0,025 |
12,00 to 13,50 |
0,70 max. |
3,50 to 5,00 |
0,30 max. |
0,08 max. |
|||||||||||||||
|
GX23CrMoV12-1 |
1.4931 |
0,20 to 0,26 |
0,40 max. |
0,50 to 0.80 |
0,030 |
0,020 |
11,30 to 12,20 |
1,00 to 1,20 |
1,00 max |
0,30 max. |
0,25 to 0,35 |
W: 0.50 max. |
||||||||||||||
|
GX4CrNiMo16-5-1 |
1.4405 |
0,06 max |
0,80 max. |
1,00 max. |
0,035 |
0,025 |
15,00 to 17,00 |
0,70 to 1,50 |
4,00 to 6,00 |
0,30 max. |
0,08 max. |
|||||||||||||||
‘to be continued’
Table 2 (concluded)
|
Austenitic and austenitic-ferritic |
Designation |
C |
Si |
Mn |
P Max. |
S max. |
Cr |
Mo |
Ni |
Cu |
N |
V |
Others |
|||||||||||||
|
Name |
Number |
|||||||||||||||||||||||||
|
GX2CrNi19-11 |
1.4309 |
0,030 max. |
1,50 max |
2,00 max. |
0,035 |
0,025 |
18,00 to 20,00 |
9,00 to 12,00 |
0,50 max. |
0,20 max. |
||||||||||||||||
|
GX5CrNi19-lO |
1.4308 |
0,07 max. |
1,50 max |
1,50 max. |
0,040 |
0,030 |
18,00 to 20,00 |
8,00 to 11,00 |
0,50 max. |
|||||||||||||||||
|
GX5CrNiNb19-11 |
1.4552 |
0,07 max. |
1,50 max. |
1,50 max. |
0,040 |
0,030 |
18,00 to 20,00 |
9,00 to 12,00 |
0,50 max. |
Nb d |
||||||||||||||||
|
GX2CrNiMo19-11-2 |
1.4409 |
0,030 max |
1,50 max. |
2,00 max. |
0,035 |
0,025 |
18,00 to 20,00 |
2,00 to 2,50 |
9,00 to 12,00 |
0,50 max. |
0,20 max |
- |
||||||||||||||
|
GX5CrNiMo 19-11-2 |
1.4408 |
0,07 max |
1,50 max |
1,50 max. |
0,040 |
0,030 |
18,00 to 20,00 |
2,00 to 2,50 |
9,00 to 12,00 |
0,50 max. |
||||||||||||||||
|
GX5CrNiMoNb19-11- 2 |
1.4581 |
0,07 max. |
1,50 max |
1,50 max. |
0,040 |
0,030 |
18,00 to 20,00 |
2,00 to 2,50 |
9,00 to 12,00 |
0,50 max. |
Nb d |
|||||||||||||||
|
GX2NiCrMo28-20-2 |
1 4458 |
0,030 max. |
1,00 max. |
2,00 max. |
0,035 |
0,025 |
19,00 to 22,00 |
2,00 to 2,50 |
26,00 to 30,00 |
2,00 max. |
0,20 max. |
|||||||||||||||
|
GX10NiCrSiNb32-20 |
1 4859 |
0,05 to 0,15 |
0,50 to 1,50 |
2,00 max. |
0,040 |
0,030 |
19,00 to 21,00 |
0,50 max |
31,00 to 33,00 |
0,50 max |
- |
Nb 0,5 to 1,5 |
||||||||||||||
|
GX2CrNiMoN22-5-3 |
1 4470 |
0,030 max. |
1,00 max. |
2,00 max. |
0,035 |
0,025 |
21,00 to 23,00 |
2,50 to 3,50 |
4,50 to 6,50 |
0,50 max. |
0,12 to 0,20 |
|||||||||||||||
|
GX2CrNiMoCuN25-6- 3-3 |
1.4517 |
0,030 max. |
1,00 max. |
1,50 max. |
0,035 |
0,025 |
24,50 to 26,50 |
2,50 to 3,50 |
5,00 to 7,00 |
2,75 to 3,50 |
0,12 to 0,22 |
|||||||||||||||
|
GX2CrNiMoN25-7-3 |
1.4417 |
0,030 max |
1,00 |
1,50 |
0,030 |
0,020 |
24,00 to 26,00 |
3,00 to 4.00 |
6,00 to 8,50 |
1,00 max. |
0,15 to 0,25 |
W= 1,00 max |
||||||||||||||
|
GX2CrNiMoN26-7-4 e |
1.4469 |
0,030 max |
1,00 max. |
1,00 max. |
0,035 |
0,025 |
25,00 to 27,00 |
3,00 to 5,00 |
6,00 to 8,00 |
1,30 max. |
0,12 to 0,22 |
|||||||||||||||
a For castings of ruling thickness < 28 mm, 0,030 S % is permitted.
b Cr ♦ Mo + Ni + V + Cu < 1,00 %
For each reduction of 0,01 % below the specified maximum carbon content, an increase of 0,04 % manganese above the specified maximum content is permitted up to a maximum of 1,40 %
Niobium: The Nb content shall be between 8 times the C content % present of the alloy and 1 % max
For this steel grade a minimum value of the "pitting index" may be required as Pi = Cr + 3,3 Mo + 16N > 40.
Table 3 — Mechanical properties at room temperature
|
Ferritic and martensitic |
Designation |
Heat treatment a |
Thickness t mm |
Tensile test |
Impact test |
|||||||
|
*p0,2 MPa* min. |
D Ь Лр1,0 MPa* min |
лт MPa* |
A % min. |
KV J min. |
||||||||
|
Name |
Number |
Symbol c |
Normalizing (+N)or Quenching (+Q) or solution annealing (+AT) °С |
Tempering eC |
||||||||
|
GP240GH |
1.0619 |
+ N |
900 to 980 |
і < 100 |
240 |
420 to 600 |
22 |
27 |
||||
|
+ QT |
890 to 980 |
600 to 700 |
z< 100 |
240 |
420 to 600 |
22 |
40 |
|||||
|
GP280GH |
1 0625 |
+ N |
900 to 980 |
t< 100 |
280 |
480 to 640 |
22 |
27 |
||||
|
+ QT |
890 to 980 |
600 to 700 |
I < 100 |
280 |
480 to 640 |
22 |
35 |
|||||
|
Gl7Mn5 |
1.1131 |
+ QT |
890 to 980 |
600 to 700 |
/<50 |
240 |
450 to 600 |
24 |
||||
|
G20Mn5 |
1.6220 |
+ N |
900 to 980 |
/<30 |
300 |
480 to 620 |
20 |
|||||
|
+ QT |
900 to 940 |
610 to 660 |
i< 100 |
300 |
500 to 650 |
22 |
||||||
|
G18Mo5 |
1.5422 |
+ QT |
920 to 980 |
650 to 730 |
/< 100 |
240 |
440 to 790 |
23 |
||||
|
G20Mo5 |
1.5419 |
+ QT |
920 to 980 |
650 to 730 |
/<100 |
245 |
440 to 590 |
22 |
27 |
|||
|
G17CrMo5-5 |
1.7357 |
+ QT |
920 to 960 |
680 to 730 |
/< 100 |
315 |
490 to 690 |
20 |
27 |
|||
|
G17CrMo9-10 |
1.7379 |
+ QT |
930 to 970 |
680 to 740 |
/< 150 |
400 |
590 to 740 |
18 |
40 |
|||
|
G12MoCrV5-2 |
1.7720 |
+ QT |
950 to 1 000 |
680 to 720 |
/ S 100 |
295 |
510 to 660 |
17 |
27 |
|||