Табл. 1-11. (Измененная редакция, Изм. №1).
Таблица 11а
Материал | Давление кислорода, МПа (кгс/см2), не более | ||||||||||||
при τ0=2·104 ч и контакте типа | при τ0=2·105 ч и контакте типа | ||||||||||||
1,a | 1,b | 1,a | 1,b | ||||||||||
при толщине δ, мм, не более | |||||||||||||
1 | 2 | 4 | 1 | 2 | 4 | 1 | 2 | 4 | 1 | 2 | 4 | ||
Резина В-14, В-14-1, Н-1, Н-10, Н-24 | 24,0 (240) | 14,0 (140) | 11,0 (110) | 27,0 (270) | 18,0 (180) | 12,0 (120) | 8,0 (80) | 4,8 (48) | 4,0 (40) | 10,0 (100) | 6,4 (64) | 4,8 (48) | |
Резина ТМКЩ по ГОСТ 7338-77 | |||||||||||||
Резина ИРП-1136 | 42,0 (420) | 28,0 (280) | 20,0 (200) | 42,0 (420) | 30,0 (300) | 22,0 (220) | 28,0 (280) | 18,0 (180) | 10,0 (100) | 30,0 (300) | 20,0 (200) | 12,0 (120) | |
Резина № 52-775 | 42,0 (420) | 32,0 (320) | 42,0 (420) | 34,0 (340) | 42,0 (420) | 24,0 (240) | 16,0 (160) | 42,0 (420) | 26,0 (260) | 18,0 (180) | |||
Капроновая смола | 26,0 (260) | 17,0 (170) | 13,0 (130) | 28,0 (280) | 20,0 (200) | 14,0 (140) | 9,6 (96) | 6,4 (64) | 4,8 (48) | 12,0 (120) | 8,0 (80) | 6,4 (64) | |
Поликарбонатная смола (дифлон) | |||||||||||||
Листовая фибра по ГОСТ 14613-83 | |||||||||||||
Фторопласт-3 по ГОСТ 13744-87 | 42,0 (420) | 26,0 (260) | 18,0 (180) | 42,0 (420) | 28,0 (280) | 20,0 (200) | 26,0 (260) | 16,0 (160) | 9,6 (96) | 28,0 (280) | 18,0 (280) | 10,0 (100) | |
Паронит ПОН по ГОСТ 481-80 | |||||||||||||
Фторопласт-4 по ГОСТ 10007-80 | 42,0 (420) | 30,0 (300) | 22,0 (220) | 42,0 (420) | 32,0 (320) | 24,0 (240) | 30,0 (300) | 20,0 (200) | 12,0 (120) | 32,0 (320) | 22,0 (220) | 14,0 (140) | |
Антифрикционные материалы на основе фторопласта-4: Ф4К20, АФГ-80ВС, АФГМ | |||||||||||||
Герметик 5Ф-13К | 32,0 (320) | 22,0 (220) | - | 36,0 (360) | 24,0 (240) | - | 14,0 (140) | 10,0 (100) | - | 16,0 (160) | 12,0 (120) | - | |
Герметик УТ-31, УТ-30М по ГОСТ 13489-79 | 22,0 (220) | 12,0 (120) | - | 26,0 (260) | 18,0 (180) | - | 7,0 (70) | 4,8 (48) | - | 9,0 (90) | 6,4 (64) | - |
Таблица 11б
Материал | Давление кислорода , МПа (кгс/см2), не более, при контакте типа 2 | ||||||||||
τ0=2·104 | τ0=2·105 | ||||||||||
Толщина δ или диаметр d, мм, не более | |||||||||||
2 | 3 | 4 | 7 | 10 | 2 | 3 | 4 | 7 | 10 | ||
Резина В-14, В-14-1, Н-1, Н10, Н-24 | 14,0 (140) | 15,0 (150) | 11,0 (110) | 7,0 (70) | 5,0 (50) | 6,4 (64) | 5,0 (50) | 4,5 (45) | 3,5 (35) | 2,4 (24) | |
Резина ТКМЩ по ГОСТ 7338-77 | |||||||||||
Резина ИРП-1136 | 28,0 (280) | 24,0 (240) | 20,0 (200) | 16,0 (160) | 12,0 (160) | 18,0 (180) | 13,0 (130) | 10,0 (100) | 8,0 (80) | 6,4 (64) | |
Капроновая смола | 18,0 (180) | 16,0 (160) | 14,0 (140) | 9,6 (96) | 7,0 (70) | 8,0 (80) | 7,0 (70) | 6,4 (64) | 5,0 (50) | 3,5 (35) | |
Поликарбонатная смола (дифлон) | |||||||||||
Фторопласт-3 по ГОСТ 13744-87 | 28,0 (280) | 24,0 (240) | 18,0 (180) | 14,0 (140) | 10,0 (100) | 18,0 (180) | 13,0 (130) | 9,0 (90) | 7,0 (70) | 5,0 (50) | |
Фторопласт-4 по ГОСТ 10007-80 | 36,0 (360) | 32,0 (320) | 24,0 (240) | 18,0 (180) | 12,0 (120) | 20,0 (200) | 16,0 (160) | 12,0 (120) | 10,0 (100) | 8,0 (80) | |
Антифрикционные материалы на основе фторопласта-4: Ф4К20, АФГ-80ВС, АФГМ | |||||||||||
Сальниковая набивка АФТ по ГОСТ 5152-84 | 42,0 (420) | 36,0 (360) | 42,0 (420) | 38,0 (380) | 30,0 (300) |
Табл. 11а, 11б. (Введены дополнительно, Изм. № 1).
Таблица 12
Группа Б
Материал | Давление кислорода, МПа (кгс/см2), не более | |||||||||||||
при τ0=2·104 ч и контакте типа | при τ0=2·105 ч и контакте типа | |||||||||||||
3,a | 3,b | 3,c | 3,a | 3,b | 3,c | |||||||||
d, мм, не более | δ, мм, не более | d, мм, не более | δ, мм, не более | |||||||||||
5 | 10 | 15 | 3 | 6 | 8 | 5 | 10 | 15 | 3 | 6 | 8 | |||
Резина В-14, В-4-1, Н-1, Н-10 | 1,6 (16) | 12,5 (125) | 10,0 (100) | 2,4 (24) | 12,5 (125) | 10,0 (100) | 2,4 (24) | 0,6 (6) | 5,0 (50) | 4,0 (40) | 1,0 (10) | 5,0 (50) | 4,0 (40) | 1,5 (15) |
Резина ТМКЩ по ГОСТ 7338-77 | ||||||||||||||
Поликарбонатная смола (дифлон) | ||||||||||||||
Капроновая смола | ||||||||||||||
Фторопласт-3 по ГОСТ 13744-87 | 5,0 (50) | 30,0 (300) | 25,0 (250) | 12,0 (120) | 30,0 (300) | 25,0 (250) | 12,0 (120) | 1,6 (16) | 10,0 (100) | 8,0 (80) | 4,0 (40) | 12,0 (120) | 8,0 (80) | 4,0 (40) |
Фторопласт-4 по ГОСТ 10007-80 | 10,0 (100) | 32,0 (320) | 28,0 (280) | 15,0 (150) | 32,0 (320) | 28,0 (280) | 12,0 (120) | 3,2 (32) | 12,0 (120) | 9,0 (90) | 6,4 (64) | 15,0 (150) | 9,0 (90) | 6,4 (64) |
Резина ИРП-1136 | 6,4 (64) | 30,0 (300) | 25,0 (250) | 13,0 (130) | 30,0 (300) | 25,0 (250) | 13,0 (130) | 2,0 (20) | 12,0 (120) | 8,0 (80) | 4,8 (48) | 14,0 (140) | 8,0 (80) | 4,8 (48) |
Резина № 52-775 | 10,0 (100) | 36,0 (360) | 30,0 (300) | 16,0 (160) | 32,0 (320) | 30,0 (300) | 14,0 (140) | 3,6 (36) | 14,0 (140) | 10,0 (100) | 6,4, (64) | 16,0 (160) | 10,0 (100) | 6,4 (64) |
Материалы на основе фторопласта-4: АФГМ, АФГ-80ВС, Ф4К20, ФКН-7, ФКН-14,ФН-1 | 10,0 (100) | 32,0 (320) | 28,0 (280) | 15,0 (150) | 36,0 (360) | 28,0 (280) | 12,0 (120) | 3,2 (32) | 12,0 (120) | 9,0 (90) | 6,4 (64) | 15,0 (150) | 9,0 (90) | 6,4 (64) |
Таблица 13
Группа Б
Материал | Давление кислорода, МПа (кгс/см2), не более, при τ0=2·104 ч, при типе контакта | ||
4, a** | 4, b | 4,c* | |
Резина Н-1, Н-10, Н-24 | 0,45 (4,5) | 2,4 (24) | 15,0 (150) |
Резина ИРП-1136 | 1,6 (16) | 4,8 (48) | 28,0 (280) |
Резина № 52-775 | 2,4 (24) | 6,4 (64) | 36,0 (360) |
__________________ *Материал покрыт латунной или медной пленкой толщиной 0,1÷0,2 мм. **Для мембран кислородных редукторов при установке на входе в редуктор металлокерамических фильтров допускаемое давление увеличивается до 2,5 МПа (25кгс/см2). |
Табл. 12, 13. (Измененная редакция, Изм. №1).
Таблица 14
Группа В
Материал | Давление кислорода, МПа (кгс/см2), не более, при скорости потока, м/с не более* | ||||
50 | 30 | 16 | 6 | 3 | |
Углеродистая сталь по ГОСТ 380-71, ГОСТ 1050-74 и легированная сталь по ГОСТ 19281-73, ГОСТ 4543-71 | - | 1,6 (16) | 4,0 (40) | 10,0 (100) | 25,0 (250) |
Алюминиевые сплавы по ГОСТ 2685-75, ГОСТ 4784-74 | 1,6 (16) | 4,0 (40) | 10,0 (100) | 42,0 (420) | |
Коррозионностойкая сталь по ГОСТ 5632-72 | |||||
Медь, сплавы на основе меди и никеля по ГОСТ 617-72, ГОСТ 859-78, ГОСТ 493-79, ГОСТ 5017-74, ГОСТ 15527-70, ГОСТ 17711-80, ГОСТ 18175-78, ГОСТ 492-73 | 42,0 (420) | ||||
____________________ *В местах местных сужений трубопроводов (на длине не более 30 диаметров трубопроводов) для установки регулирующих и других устройств расчетную скорость потока допускается увеличивать до 60 м/с независимо от материала трубопровода. |
Таблица 15
Группа В
Материал | Давление кислорода, МПа (кгс/см2), не более | В арматуре отключения КИП (Dy≤6 мм) | |||||||||||||||||
в запорной арматуре | в регулирующей арматуре | ||||||||||||||||||
при управлении | |||||||||||||||||||
местном | дистанционном4 | местном | дистанционном4 | ||||||||||||||||
корпус | детали запорного устройства | корпус | детали запорного устройства | корпус | детали запорного устройства | корпус | детали запорного устройства | корпус | Шпиндель с запорным конусом ≥60°, детали запорного устройства | ||||||||||
Алюминиевые сплавы1 по ГОСТ 2685-75, ГОСТ 4784-74 | 1,6 (16) | Не применяются | |||||||||||||||||
Чугуны по ГОСТ 26358-84 | 1,6 (16) | 1,6 (16) | 1,6 (16) | 0,6 (6) | 1,6 (16) | 1,6 (16) | 1,6 (16) | ||||||||||||
Углеродистые стали по ГОСТ 380-71, ГОСТ 1050-74 и легированные стали по ГОСТ 4543-71, ГОСТ 19281-72 | |||||||||||||||||||
Нержавеющие стали по ГОСТ 5632-725 | 6,4 (64) | 6,42 (64) | 6,4 (64) | 16,52 (165) | 4,0 (40) | 4,03 (40) | 6,4 (64) | 16,52 (165) | 25,0 (250) | ||||||||||
__________________ 1 Детали запорных устройств из алюминиевых сплавов изготавливают только плоскими. 2 При давлениях св. 4 МПа (40 кгс/см2) одна из деталей должна быть из сплавов на основе меди. 3 При давлениях св. 1,6 МПа (16 кгс/см2) одна из деталей должна быть из сплавов на основе меди. 4 Предохранительная арматура (клапаны и мембраны) должна изготовляться как запорная с дистанционным управлением. 5 Арматура из углеродистых сталей и чугунов с покрытием из органо-силикатных материалов приравнивается к арматуре из нержавеющих сталей. |